Biaxially oriented film base resin
Basic Resin for BOPP Film
Product performance:
This product is mainly composed of liquid phase propylene bulk polymerization, or binary random copolymerized polypropylene produced by liquid phase propylene and gas phase ethylene, and binary randomness produced by liquid phase propylene, butene and gas phase ethylene. Copolymerized polypropylene, the product is in the shape of cylindrical particles. The product has good strength, wear resistance, impact resistance, good stress crack resistance, excellent chemical stability and insulation, and the heat sealing temperature and transparency of the ternary copolymerized polyene are lower than the binary Random copolymerization is better.
The main purpose:
Mainly used in the production of various biaxially oriented films.
Typical product value | |||
Brand | F 500EP | F500EPS | I180E |
Melt flow rate g / 10min | 5 . 0 | 5 . 0 | 1 . 8 |
Tensile yield strength MPa ≥ | 19 . 5 | 19 . 5 | 23 . 5 |
æ³ arm beam impact strength (23 °C) J / m ≥ | 35 . 0 | 35 . 0 | 19 . 6 |
Flexural modulus GPa ≥ | 0 . 43 | 0 . 43 | 0 . 63 |
Vicat softening point °C≥ | 112 | 112 | |
Haze% | 2 | 2 | |
Gloss%≥ | 76 | 76 | |
Polymer type | Binary random copolymerization | Ternary random copolymerization | Random copolymerization |
processing method | Extrusion, stretching | Squeeze the mountain | Blow molding |
The main purpose | Biaxially stretched film | Biaxially stretched film | Heat shrinkable film |